Abstract:
The results of estimation of activation parameters in the region of exponential (I) and power (II) dependences of the steady-state creep rate of polycrystalline copper on stress were represented. It is shown that the elastic long-range stress produced by dislocations in region I can be determined directly from the dependence of the creep rate on the stress. An energy criterion of the transition from creep region I to region II is proposed.