Optical properties of Yb : Lu$_3$Al$_5$O$_{12}$ crystal irradiated by 4.5-MeV Si ions

W. Tang, Yu. Wang, C.-L. Jia

School of Materials Science and Physics, China University of Mining and Technology, Xuzhou 221116, Jiangsu, People’s Republic of Chin

Abstract: Compact waveguide laser sources emitting at wavelength around 1.0 $\mu$m are interesting in a multiple of application. In present work, we demonstrate a crystalline waveguide in Yb : Lu$_3$Al$_5$O$_{12}$ (Yb : LuAG) crystal irradiated by 4.5-MeV Si ions at fluences of 1.0 $\cdot$ 10$^{15}$ cm$^{-2}$. A typical “barrier-confined” waveguide geometry is confirmed by performing the prism-coupling measurement at a wavelength of 632.8 nm with transverse electric (TE) polarization, and the refractive index profile is proposed based on the dark-mode plots. Under excitation at 930 nm, the peak emission at 1030 nm is generated with a bandwidth of 14.4 nm. The fluorescence decay actions are investigated on a Jobin Yvon spectrometer. The radiative constants and peak emission cross-section values are obtained.

Keywords: Yb, Lu$_3$Al$_5$O$_{12}$, ion irradiation, optical waveguide, photoluminescence spectroscopy.

Received: 28.08.2020
Revised: 28.08.2020
Accepted: 01.09.2020

Language: English

 English version: Physics of the Solid State, 2021, 63:1, 107–112